Polyimide Tape 2 Mil – Kapton Alternative (70002)

Polyimide Tape 2 Mil – Kapton Alternative (70002)



Polyimide Film Tape (Kapton® Alternative) Information



Polyimide Film Tape (70002) is a 2 mil amber comercial grade electrical Kapton® alternative polyimide film coated with a high performance silicone adhesive. Tape is thin and conformable, with outstanding tear and abrasion resistance at elevated temperatures. Adhesive will thermoset to increase adhesion values. Leaves minimal residue when removed after manufacturing process; reduces clean-up time and minimizes rejects. Permits operation of boards during processing. Film meets UL510. Formulated to Mil Spec: MIL-P-46112b. 3″ Core.


* Masking applications where very high temperatures are involved.
* Designed for insulating coil at high temperature as well as for the products like generator, capacitor and transformer to use.

Physical Properties:

Backing   2.0 mil polyimide film (amber)
Adhesive   Silicone
Total Thickness   3.6 mil
Adhesion   21 oz/inch
Elongation   >70%
Temperature Resistance   200°C (392 í_F) / 30min.
Dielectric Strength   7000 Volts

Alternative to: Bondtec #911-325; Electro Tape #95-2; Anchor #K-350; American #304-2; Permacel #P-222; T&F #3903; Taconic #6325-02; Berry Plastics #2345-2; Tesa #4429; Ideal #9322; Solar Plus #KA105#50; Dewal #303-2.

Note: The physical properties listed above are typical test results obtained from a series of laboratory tests and should not be used for the purpose of writing specifications. Before using this product, user shall determine the suitability of the product for his/her use; and user assumes all risks and liabilities in connection therewith. All test procedures used are in accordance with ASTM and PSTC methods.

Additional information

Weight 1 lbs

1.5" (36mm), 1" (24mm), 1/2" (12mm), 1/4" (6mm), 2" (48mm), 3" (72mm), 3/4" (18mm), 3/8'' (9mm), 4" (96mm), 5/8" (15.9mm), 7/8" (22.2mm)

Pack Size

Case, Subpack, Single Roll

SKU: 70002 - Need Help? Contact Us Leave Feedback